The difference between Stainless steel hot rolled plate and cold rolled plate

/in /by

Stainless steel has excellent corrosion resistance, processing, biocompatibility and strong toughness within a wide range of temperatures, has been widely used in the petrochemical industry, atomic energy, light industry, textile, food, household appliances and other fields. Hot rolling and cold rolling are the necessary processes for stainless steel plate forming. The hot rolled plate is the raw material of cold-rolled plate, both of them will affect the microstructure of the stainless steel plate.

The hot rolling process of stainless steel is made from the slab (mainly continuous casting slab), which is heated and made from a roughing mill and finishing mill group. The hot steel from the last finishing mill is cooled by laminar flow to the specified temperature and is rolled into coils by the coiler. The steel after cooling has an oxide surface, with a black color, commonly known as “stainless steel black coil”. After annealing and pickling, the oxidized surface is removed, that is, “stainless steel white roll”. Some hot rolled stainless steel products can be used directly and some need to be processed into cold-rolled products before being used.

Stainless steel cold-rolled plate is generally the product of stainless steel hot-rolled plate with a thickness of 3.0-5.5mm after being rolled and processed by cold rolling equipment (single stand cold rolling/multi-strand cold rolling). Different processing methods and reprocessing after cold rolling can make the surface of stainless steel plate have different grades of surface finish, grain and color. There are 2D, 2B, No.3, No.4, No.4, HL, BA, TR, embossing and other surface grades in the surface processing of cold-rolled stainless steel plates. A variety of deeply processed surfaces such as electroplating, electropolishing, directional pattern, etching, shot peening, coloring, coating and its combination can be further implemented on the basis of cold rolling, in addition, the no.1 surface and pattern plate after hot rolling pickling are also included. what’s the difference between of hot rolled and cold rolled stainless steel plate?

 

Different surface qualities

Stainless steel cold-rolled plate has good surface quality, no oxide scale, a variety of surface treatments are available. Stainless steel hot rolled plate is generally No 1 treatment, with oxide skin, gray-white (pickling) or black-brown (not electroplated). The smoothness of the cold-rolled plate after electroplating is higher than that of a hot rolled plate.

 

Different prices

The toughness and surface quality of the stainless steel cold-rolled plate is higher than the hot-rolled plate, and the price is higher than the hot-rolled plate.

 

Different applications

Stainless steel cold-rolled sheet is widely used in various civil and industrial fields, including architectural decoration, products, home appliances, rail transit transportation, automobiles, elevators, containers, solar energy, precision electronics, etc. 2D, 2B, BA and grinding surface can be directly used for most products in architectural decoration, elevator, container and other industries. The cold-rolled sheet after forming or re-processing can be used in places with higher surface quality requirements, such as home appliances, rail transportation, automobiles, solar energy, precision electronics, etc.

What is Ferritic stainless steel used for?

/in /by

Ferrite stainless steel refers to the stainless steel with 11%~30%Cr and cubic crystal ferrite structure. Its high chromium content is the main element that affects its performance. The advantages of Ferritic stainless steel include low cost (without nickel), good magnetic conductivity, excellent stress corrosion resistance; Small working hardening tendency, easy to cold heading and cutting; High thermal conductivity (1.5 times that of Austenitic steel), low linear expansion coefficient (60% of Austenitic steel), but also obvious disadvantages such as poor plasticity and low strength in post-processing, easy welding cracking. Ferritic stainless steel is mainly used in oxidizing medium and nitride medium, suitable for heat exchange and heat circulation purposes, provides a wide range of applications.

 

Architecture and structure applications

Ferritic stainless steel is used as the roof and curtain wall of buildings because of its good resistance to atmospheric corrosion. High-chromium ferritic stainless steels used in coastal areas have been developed, and atmospheric corrosion-resistant stainless steels contain high levels of chromium and molybdenum and are supplemented with small amounts of niobium and titanium. The steel actually contains 22% chromium and 1.2% molybdenum. Sufficient chromium and molybdenum are necessary to improve the pitting resistance of stainless steel. The rusting area of type 304 and Type 316 austenitic stainless steel increased significantly with the increase of the number of periodic corrosion test cycles. On the contrary, the rust area of type 444 ferritic stainless steel increased slightly during the first 600 test cycles and was saturated after longer tests.

 

Automobile industry

Type 409 or 410L stainless steel is used as a vehicle exhaust emission control system material such as front pipe, center pipe and muffler due to its excellent intergranular corrosion resistance, formability and heat resistance. In recent years, the design temperature of vehicle exhaust has increased because of the catalytic conversion rate and reduction of harmful gases such as NOx, SOx and hydrocarbon (HC) emissions. However, the increased temperature of chromium carbide will produce deposits on the silencer, i.e., temperatures of 400 ~ 500℃will lead to grain boundary corrosion. Because the weld area is particularly sensitive to intercrystalline corrosion, it is necessary to improve the corrosion resistance of Ferritic stainless steel containing 12% Cr. Therefore, a new Ferritic stainless steel was developed by adding niobium to steel containing 12% Cr. It is well known that reducing carbon and nitrogen content in steel is quite effective in preventing intercrystalline corrosion. In this way, the intercrystalline corrosion resistance can be further improved by adding niobium and titanium to steel. 409L stainless steel is used as the material for the exhaust manifold of automobiles, and the exhaust temperature is designed to be about 800℃. 430J1L stainless steel is recommended when the exhaust temperature is approximately 900℃.

 

Home appliances and kitchenware

400 series ferrite stainless steel has been widely accepted in the field of household appliances and kitchenware because of its unique aesthetic properties, corrosion resistance to cleaners and disinfectants, low thermal expansion coefficient and magnetism (suitable for electromagnetic cookers). Ferritic stainless steel greatly reduces weight compared with carbon steel. Ferritic stainless steels do not contain nickel and are far more price stable than Austenitic steels, making it easier for manufacturers to manage costs, purchase and sell. The use of ferritic stainless steel is so wide, each use of the required ferrite stainless steel performance is different. Typical applications include dishwashers, electric kettles, washing machines, dustbins, kitchen drains, ovens, gas appliances, coffee makers, microwave ovens, gas stoves, cold storage, restaurant trolleys.

 

Ferritic stainless steel is also used in transportation and other industrial applications. Because it has so many advantages over carbon steel and Austenitic stainless steel, it’s excellent formability like bending, cutting and drilling making it has a wide applications. Because there are many ferritic stainless steel grades, in order to obtain good corrosion resistance, good strength and lower price, you need to choose the right grade to meet customer requirements.

Grades Chemical composition Characterize Applications
409L 11.3Cr-0.17Ti

Low C and N

 The added Ti making it has good high-temperature corrosion resistance and strength. Automobile exhaust pipes, heat exchangers, containers and other products without heat treatment after welding.
410L 13Cr

Low C

 Reduce the C based on 410, has good processing, welding deformation resistance, high-temperature oxidation resistance. Parts for mechanical construction, engine exhaust pipes, boiler combustor, burner.
430 16Cr Typical grades of ferrite steel, it has a low thermal expansion rate, excellent formability and oxidation resistance. Heat resistant appliances, burners, home appliances, tableware, kitchen sinks, external decorative materials, bolts, nuts, screen
430J1L 18-Cr0.5Cu-Nb

Low C&N

 Addition of Cu, Nb based on 430, good corrosion resistance, formability, weldability and high-temperature oxidation resistance. Building exterior decoration materials, auto parts, hot and cold water supply equipment.
436L 18Cr-1Mo-Ti、Nb、Zr

Low C&N

 Added Nb, Zr, excellent heat resistance and abrasion resistance, good processing and weldability. Washing machines, car exhausts, electronics, cooking POTS.